发热电阻浆料
  • 产品详情

 

 

产品规格书/Specification

 

产品/product:

不锈钢基材发热电阻浆料/

Stainless steel board heating Resist paste

料号/Part number:

05H11

 

 

适用范围/Application:

此产品适用于不锈钢基材加热电路使用。

The resist paste applies to stainless steel board heating resistor paste.

 

 

使用条件/Operating conditions

基材

Substrate

不锈钢基材

Stainless steel board

印刷

Printing

200-250目丝网印刷

200-250 mesh stainless screen

流平

Levelling

室温下流平5-15分钟(时间根据流平的实际情况决定)。

5-15min minutes at room temperature

干燥

Drying

通风烘箱烘烤100-150℃,10-15分钟

(烘考温度低于300℃,可根据烘烤的实际情况决定烘烤时间。)

100-150  10-15 min

烧结

Firing Condition

隧道炉空气气氛下烧结,峰值850(推荐值),10分钟。

Atmospheric firing in belt furnace with peak time of 10 Minutes at 850

Thinner

ST1001

 

 

性能/Characteristics

1. 浆料性能/Paste Characteristics

性能Characteristic

标准Standard

测试方法及条件

Test method and conditions

1

Fineness

8μm

FOG test

2

Viscosity

120-280Pa.s

Brookfield HBT utility cup and spindle (SC4-14/6R), 10rpm, 25±1

Brookfield HBT(博利飞)粘度计, 转子SC4-14/6R), 10rpm, 25±1℃

粘度可根据用户实际需要调节。

 

 

2. 烧结后特性/Characteristics after firing

1烧结条件下,膜厚8-12mm Check fired film produced under the conditions specified in 1, (Film thickness is 8-12mm.)  

 

 

 

特性

Characteristics

Standard

标准

测试方法和条件

Test method and conditions

3

外观

Appearance

紧凑,致密

Compact and unknit

Eyeballing

 

4

方阻值

Resistivity

如下表格

As below form

标准膜厚10μm

Standard film thickness is 10mm.

温度系数

TCR 

如下表格

As below form

HTCR 25-125℃

 

 

产品系列

铝基材发热电阻浆料

P/N

resistivity (Ω/□)

TCR (ppm/℃)

烧结温度

viscosity (kcps)

05H11-0R01012

0.01

1500

850

120280

05H11-0R02012

0.02

1200

05H11-0R03012

0.03

1200

05H11-0R05012

0.05

1200

05H11-0R10012

0.10

1200

05H11-0R20012

0.20

1200

05H11-0R30012

0.30

1200

05H11-0R50012

0.50

1200

05H11-1R00012

1.00

100-1200

05H11-3R00012

3.00

100-1200

05H11-4R00012

4.00

100-1200

05H11-011

10.00

0-600

05H11-021

20.00

0-600

05H11-051

50.00

0-600

05H11-101

100.00

0-600

 

 