基材

Substrate

氧化铝陶瓷，LTCC 陶瓷，叠层元件 Alumina ceramic

印刷

Printing

200-300 目丝网印刷

200-300 mesh stainless screen

干燥&烧结 Drying

&Sintering

1  单层印刷（氧化铝板）

Single layer printing(Alumina ceramic) 通风烘箱烘烤 100-150℃ , 10-15 分钟 100-150℃    10-15 min

空气下烧结，峰值 850℃（最低推荐值），2-10 小时。 (可根据实际需要调高烧结温度 850~1400℃)

Sintering in air with a peak temperature of 850°C (minimum recommended value) for 2 to 10 hours. (The sintering temperature can be adjusted upward according to actual needs from 850°C to 1400°C.)

②  多层印刷

Multilayer printing

200-500℃温度间排胶，最少 60 分钟

Binder removing, 200-500℃ , 60 mins at least

空气下烧结，峰值 850℃（最低推荐值），2-10 小时。 (可根据实际需要调高烧结温度 850~1400℃)

Sintering in air with a peak temperature of 850°C (minimum recommended value) for 2 to 10 hours. (The sintering temperature can be adjusted upward according to actual needs from 850°C to 1400°C.)

Thinner

ST-1000

性能

Characteristic

标准

Standard

测试方法及条件

Test method and conditions

1

Fineness

≤5μm

FOG test

2

Viscosity

280-530Pa.s

Brookfield HBT utility cup and spindle (SC4-14/6R), 10rpm, 25±1℃ ,

Brookfield HBT（博利飞）粘度计， 转子 SC4-14/6R), 10rpm, 25±1℃ 粘度可根据用户实际需要调节。