发热电阻浆料
  • 产品详情

产品规格书/Specification

 

产品/product:

氮化硅陶瓷发热电阻浆料/

Si3N4 ceramic board heating Resist paste

料号/Part number:

05H71

 

适用范围/Application:

此产品适用于氮化硅陶瓷加热电路使用。

The resist paste applies to Si3N4 ceramic heating resistor paste.

01H-7103电极银浆匹配使用

使用条件/Operating conditions

基材

Substrate

氮化陶瓷

 Si3N4  ceramic

印刷

Printing

200-250目丝网印刷

200-250 mesh stainless screen

流平

Levelling

室温下流平5-15分钟(时间根据流平的实际情况决定)。

5-15min minutes at room temperature

干燥

Drying

通风烘箱烘烤100-150℃,10-15分钟

烘烤温度低于300℃,可根据烘烤的实际情况决定烘烤时间。)

100-150  10-15 min

烧结

Firing Condition

隧道炉空气气氛下烧结,峰值800(推荐值),10分钟。

Atmospheric firing in belt furnace with peak time of 10 Minutes at 800

Thinner

ST1001

 

 

性能/Characteristics

1. 浆料性能/Paste Characteristics

性能Characteristic

标准Standard

测试方法及条件

Test method and conditions

1

Fineness

≤8μm

FOG test

2

Viscosity

120-280Pa.s

Brookfield HBT utility cup and spindle (SC4-14/6R), 10rpm, 25±1

Brookfield HBT(博利飞)粘度计, 转子SC4-14/6R), 10rpm, 25±1℃

粘度可根据用户实际需要调节。

 

 

2. 烧结后特性/Characteristics after firing

1烧结条件下,膜厚8-12mm Check fired film produced under the conditions specified in 1, (Film thickness is 8-12mm.) 

 

 

 

特性

Characteristics

Standard

标准

测试方法和条件

Test method and conditions

3

外观

Appearance

紧凑,致密

Compact and unknit

Eyeballing

 

4

方阻值

Resistivity

如下表格

As below form

标准膜厚10μm

Standard film thickness is 10mm.

温度系数

TCR

如下表格

As below form

HTCR 25-125℃

 

 

产品系列

氧化陶瓷发热电阻浆料

Si3N4 ceramic board heating Resist paste

P/N

resistivity (Ω/□)

TCR (ppm/℃)

烧结温度℃

Sintering

viscosity (kcps)

05H71-0R02012

0.02

1200

850

120-280

05H71-0R03012

0.03

1200

05H71-0R05012

0.05

1200

05H71-0R10012

0.10

1200

05H71-0R20012

0.20

1200

05H71-0R30012

0.30

1200

05H71-0R50012

0.50

1200

05H71-1R00012

1.00

1200

05H71-3R00012

3.00

1200

05H71-4R00012

4.00

1200

05H71-5R00012

5.00

1200

05H71-011

10.00

1200

 

Sintering

保存条件,有效期/Storage condition and Term of validity

产品应在5-25℃的环境温度下密封储存,有效期为产品发货之日起六个月。

 

包装方式/Packaging method

1000g/, 1000g/can

 